1836 FONDO FINITURA ACRILICO SEMI OPACO DTM

Industry

primer-finish

Two-pack anticorrosion primer-finish, adhesion to iron, galvanised steel plate and aluminium

Semi-matt base-finish based on acrylic resin and isocyanic adduct. It is suitable for products in general when a good anticorrosive power is to be obtained with a high aesthetic appearance finish and when excellent resistance to the exterior is required. It has a good solidity at high temperatures (90/100°C) for a continuous service of three hours. The light colors (pure white) if submitted for long periods at such temperatures, could present a slight yellowing.

→ Semi-matt
→ Direct adhesion
→ Anticorrosive

Application

Suitable for iron, galvanised steel plate, aluminium, PVC, fibreglass.

Tools
Spray gun

Technical data

Dry film aspect

semi-gloss

Sheen

35 - 40 Gloss 60°

Oven drying

60 min - 60°C

Dust free

10 min

Pot-Life

90 min

Touch dry

2 - 3 h

Dry through

24 h

Recommended thickness

See TDS

Flash-off

5 - 10 min

→ Dilution

10 - 15% with 1611 DIL EXTRA PU

→ Cover rate

6 - 7 m²/kg with 2 coats referred to a dry thickness of about 50 μm

Unit size
0000 Converter

14 kg

3,5 kg

Colours

20 kg (min. order 6 pcs)

Note

Curing ratio: 100:15 in weight
Hardener B: 1873 for ACRYLIC/PU NON-YELLOWING

Technical data sheet

it

en

Share on

Suggested products

1831 FONDO FINITURA SEMILUCIDO

One-layer primer-finish for use on structural work

1841 IMPAZINC

Enamel with direct adhesion to galvanised steel plate, light alloys, ABS, PVC

1949 FONDO FINITURA ACRILICO SEMI LUCIDO DTM

Two-pack primer-finish, adhesion to iron, galvanised steel plate and aluminium

1736 FONDO FINITURA ACRILICO OPACO DTM

Two-pack anticorrosion primer-finish, adhesion to iron, galvanised steel plate and aluminium